The MARBAIN® Advantage

Fisher Barton developed MARBAIN to give our customers the hardest, strongest, longest-lasting, and best material in the industry! MARBAIN is material resulting from our exclusive, patented heat-treating process. Many components and all blades are heat-treated, but no blade or component in the industry can advertise the hardness offered by Fisher Barton. The MARBAIN heat-treating process is a controlled, proprietary operation that creates ultra-hard properties without the brittleness associated with typical high Rockwell “C” hardness levels.

Market-recognized premium mower blade material for 20+ years!

Blades manufactured from our AISI 10B38 base material with our MARBAIN process are stronger, harder (7-12 Rc points harder than industry norm), and last longer than competitive offerings, while providing a cost-effective alternative to abrasion resistant steel and other manufacturing materials.

Result: Hardnesses of between 48-52 Rc were achieved improving wear resistance by 33% over conventional Austempering processes.

Laseredge

Fisher Barton MARBAIN® Lawn Mower Blades Undergo Severe Testing

Marbain Lasts Longer

Marbain Hardness

Features & Benefits

  • Exclusive, unmatched proprietary patented heat treat process
  • High hardness levels never thought possible!
  • No increased brittleness at 48-52 Rockwell “C”
  • Greater yield strength—the strongest mower blades on the market
  • Thinner/lighter components
  • No loss in wear resistance or field life
  • MARBAIN steel blades are stronger, harder, and require less time sharpening
  • Potential reduced weight
  • Faster start/stop
  • Less wear on PTO clutch break
  • Lower fuel consumption
  • Guaranteed impact toughness in every rotary cutter blade – 2.07 Kilogram force-meter (15 ft. lbs.) minimum!
  • Product traceability to the steel mill and all metallurgical tests
  • Austempered, not Quench/Tempered
  • Cost-effective even with superior material
  • Better impact toughness (ANSI-S483 compliant)
  • Fisher Barton leads the Agricultural Equipment Manufacturers blade working group.
  • Fisher Barton proposed standards changes in 1992 that are now adopted in the new standards.

Austempering Heat Treatment

Austempering Heat Treatment

The unique Fisher Barton austempering heat treatment process produces high hardness parts that are extremely ductile. The ductility is achieved through the elimination of quench cracks (macro and micro) that are common in most conventional quench and temper heat treat processes. When large (macro) cracks occur it is usually obvious. However, the micro cracks in the atomic structure are virtually impossible to detect. These defects inhibit ductility by setting up barriers in the atomic structure, preventing the material to flow plastically.

When steel is heat treated we expect: high hardness, wear resistance, strength and toughness. A transformation of the metals’ atomic structure occurs. During heat treating the metal is raised to a high temperature of 843 degrees Celsius (1550 degrees Fahrenheit) and is transformed to austenite (FCC), the highest density phase. The metal is cooled causing the austenitic phase to be transformed into three possible atomic arrangements or phases: BCC, BCT and Orthorhombic. In all of these transformation phases, expansion and a decrease in density of the metal occurs. It is this expansion that results in quench crack problems.

The conventional quench and temper process produces martensite (BCT), a low-density, hard, and very brittle phase. There are two factors that can cause quench cracks during the formation of martensite. They are reduced plasticity at low temperatures and the instantaneous shear characteristics of the transformation. Because martensite is not ductile at low quench temperatures and because of its rapid shear formation nature, the continuing transformation of austenite (FCC) to martensite (BCT)sets up very high stress factors in the initially transformed martensitic structure. When the martensitic phase can no longer absorb additional expansion stresses, cracks (macro and micro) can occur.

Learn why MARBAIN is the best blade material on the market.

Tell Us About Your Project

Do you have a specific project you’re ready to discuss? Use our quote request form to start the process.